Influence of Cobalt Precursor on Efficient Production of Commercial Fuels over FTS Co/SiC Catalyst
β-SiC-supported cobalt catalysts have been prepared from nitrate, acetate, chloride and citrate salts to study the dependence of Fischer–Tropsch synthesis (FTS) on the type of precursor. Com/SiC catalysts were synthetized by vacuum-assisted impregnation while N2 adsorption/desorption, XRD, TEM, TPR,...
| Autores: | , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2016 |
| País: | España |
| Institución: | Universidad de Castilla-La Mancha |
| Repositorio: | RUIdeRA. Repositorio Institucional de la UCLM |
| OAI Identifier: | oai:ruidera.uclm.es:10578/29637 |
| Acceso en línea: | http://hdl.handle.net/10578/29637 |
| Access Level: | acceso abierto |
| Palabra clave: | Fischer–Tropsch β-SiC support Cobalt precursors Commercial fuels Soporte de β-SiC Precursores de cobalto Combustibles comerciales |
| Sumario: | β-SiC-supported cobalt catalysts have been prepared from nitrate, acetate, chloride and citrate salts to study the dependence of Fischer–Tropsch synthesis (FTS) on the type of precursor. Com/SiC catalysts were synthetized by vacuum-assisted impregnation while N2 adsorption/desorption, XRD, TEM, TPR, O2 pulses and acid/base titrations were used as characterization techniques. FTS catalytic performance was carried out at 220 °C and 250 °C while keeping constant the pressure (20 bar), space velocity (6000 Ncm3/g·h) and syngas composition (H2/CO:2). The nature of cobalt precursor was found to influence basic behavior, extent of reduction and metallic particle size. For β-SiC-supported catalysts, the use of cobalt nitrate resulted in big Co crystallites, an enhanced degree of reduction and higher basicity compared to acetate, chloride and citrate-based catalysts. Consequently, cobalt nitrate provided a better activity and selectivity to C5+ (less than 10% methane was formed), which was centered in kerosene-diesel fraction (α = 0.90). On the contrary, catalyst from cobalt citrate, characterized by the highest viscosity and acidity values, presented a highly dispersed distribution of Co nanoparticles leading to a lower reducibility. Therefore, a lower FTS activity was obtained and chain growth probability was shortened as observed from methane and gasoline-kerosene (α = 0.76) production when using cobalt citrate |
|---|