Effect of high pressure on the reducibility and dispersion of the active phase of Fischer-Tropsch catalysts
The effect of high pressure on the reducibility and dispersion of oxides of Co and Fe supported on -Al2O3, SiO2, and TiO2 has been studied. The catalysts, having a nominal metal content of 10 wt.%, were prepared by incipient wetness impregnation of previously calcined supports. After drying at 60 °C...
| Autores: | , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2019 |
| País: | España |
| Institución: | Universidad Pública de Navarra |
| Repositorio: | Academica-e. Repositorio Institucional de la Universidad Pública de Navarra |
| OAI Identifier: | oai:academica-e.unavarra.es:2454/36271 |
| Acceso en línea: | https://hdl.handle.net/2454/36271 |
| Access Level: | acceso abierto |
| Palabra clave: | Fischer-Tropsch Supported iron oxide Supported cobalt oxide Reducibility Dispersion |
| Sumario: | The effect of high pressure on the reducibility and dispersion of oxides of Co and Fe supported on -Al2O3, SiO2, and TiO2 has been studied. The catalysts, having a nominal metal content of 10 wt.%, were prepared by incipient wetness impregnation of previously calcined supports. After drying at 60 °C for 6 h and calcination at 500 °C for 4 h, the catalysts were reduced by hydrogen at two pressures, 1 and 25 bar. The metal reduction was studied by temperature-programmed reduction up to 750 °C at the two pressures, and the metal dispersion was measured by CO chemisorption at 25 °C, obtaining values between 1% and 8%. The physicochemical characterization of these materials was completed by means of chemical analysis, X-ray diffraction, N2 adsorption-desorption at -196 °C and scanning electron microscopy. The high pressure lowered the reduction temperature of the metal oxides, improving their reducibility and dispersion. The metal reducibility increased from 42%, in the case of Fe/Al2O3 (1 bar), to 100%, in the case of Fe/TiO2 (25 bar). |
|---|