Correlation between local structure and magnetic behavior in co-sputtered Tb_xFe_(73)Ga_(27-x) (7 ≤ x ≤11) thin films
We report on the evolution of the microstructure of Tb-Fe-Ga films deposited by co-sputtering from Tb_(33)Fe_(67) and Fe_(72)Ga_(28) targets. The sputtering power was fixed (90 W) in the Fe_(72)Ga_(28) whereas it was increased from 50 to 90 W in the Tb_(33)Fe_(67) target resulting on Tb_xFe_(73)Ga_(...
| Autores: | , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2017 |
| País: | España |
| Institución: | Universidad Complutense de Madrid (UCM) |
| Repositorio: | Docta Complutense |
| Idioma: | inglés |
| OAI Identifier: | oai:docta.ucm.es:20.500.14352/18270 |
| Acceso en línea: | https://hdl.handle.net/20.500.14352/18270 |
| Access Level: | acceso abierto |
| Palabra clave: | 538.9 Sputtering Iron alloys x-ray Absorption fine structure Magnetic properties Física de materiales Física del estado sólido 2211 Física del Estado Sólido |
| Sumario: | We report on the evolution of the microstructure of Tb-Fe-Ga films deposited by co-sputtering from Tb_(33)Fe_(67) and Fe_(72)Ga_(28) targets. The sputtering power was fixed (90 W) in the Fe_(72)Ga_(28) whereas it was increased from 50 to 90 W in the Tb_(33)Fe_(67) target resulting on Tb_xFe_(73)Ga_(27-x) layers with 7 ≤ x ≤ 11. The local structure was determined by means of x-ray absorption fine structure spectroscopy at Fe-K, Ga-K and Tb-L_(3) edges. The increase of Tb in the alloy promotes the phase segregation that produces a larger amount of the TbFe_2 structural phase. The structural results have been correlated with the magnetic characterization that shows the enhancement of the out-of-plane component of the magnetization. |
|---|