Microstructure development in mixes of calcium aluminate cement with silica fume or fly ash
The most widely identified degradation process suffered by calcium aluminate cement (CAC) is the so-called conversion of hexagonal calcium aluminate hydrate to cubic form. This conversion is usually followed by an increase in porosity determined by the different densities of these hydrates and the s...
| Autores: | , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión aceptada para publicación |
| Fecha de publicación: | 2009 |
| País: | España |
| Institución: | Consejo Superior de Investigaciones Científicas (CSIC) |
| Repositorio: | DIGITAL.CSIC. Repositorio Institucional del CSIC |
| OAI Identifier: | oai:digital.csic.es:10261/49812 |
| Acceso en línea: | http://hdl.handle.net/10261/49812 |
| Access Level: | acceso abierto |
| Palabra clave: | Calcium Aluminate cements Fly ash Microstructure Silica fume TG-DTA WAXS |
| Sumario: | The most widely identified degradation process suffered by calcium aluminate cement (CAC) is the so-called conversion of hexagonal calcium aluminate hydrate to cubic form. This conversion is usually followed by an increase in porosity determined by the different densities of these hydrates and the subsequent loss of strength. Mixes of calcium aluminate cement (CAC) and silica fume (SF) or fly ash (FA) represent an interesting alternative for the stabilization of CAC hydrates, which might be attributed to a microstructure based mainly on aluminosilicates. This paper deals with the microstructure of cement pastes fabricated with mixtures CAC-SF and CAC-FA and its evolution over time. Thermal analysis (DTA/TG), X-ray diffraction (XRD) and mid-infrared spectroscopy (FTIR) have been used to assess the microstructure of these formulations. |
|---|