Characterization of nickel doped Zn7Sb2O12 spinel phase using Rietveld refinement
Zn7Sb2O12 is known to adopt an inverse spinel crystal structure, in which Zn2+ occupies the eight tetrahedral positions and Sb5+ and Zn2+ randomly occupy the 16 octahedral positions. Samples of Zn7-xNixSb2O12 (X = 0, 1, 2, 3, and 4) were synthesized using a modified polymeric precursor method, known...
| Autores: | , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2003 |
| País: | Brasil |
| Institución: | Universidade Estadual Paulista (UNESP) |
| Repositorio: | Repositório Institucional da UNESP |
| Idioma: | inglés |
| OAI Identifier: | oai:repositorio.unesp.br:11449/39225 |
| Acceso en línea: | http://dx.doi.org/10.1154/1.1572486 http://hdl.handle.net/11449/39225 |
| Access Level: | acceso abierto |
| Palabra clave: | spinel structure X-ray diffraction Rietveld method Pechini method |
| Sumario: | Zn7Sb2O12 is known to adopt an inverse spinel crystal structure, in which Zn2+ occupies the eight tetrahedral positions and Sb5+ and Zn2+ randomly occupy the 16 octahedral positions. Samples of Zn7-xNixSb2O12 (X = 0, 1, 2, 3, and 4) were synthesized using a modified polymeric precursor method, known as the Pechini method. The crystal structure of the powders was characterized by Rietveld refinement with X-ray diffraction data. The results show that for X = 0, 1, and 2 Ni substitutes for Zn2+ in the octahedral sites, and that for X = 3 and 4 it is assumed that Ni2+ replaces Zn2+ ions in both the octahedral and tetrahedral positions. It is also observed for x = 3 and 4 the formation of two spinel phases. (C) 2003 International Centre for Diffraction Data. |
|---|