SnO2 dense ceramic microwave sintered with low resistivity
The Hall-Héroult process is used for alumina reduction by the use of graphite anodes even though it involves a high emission of carbon dioxide (CO2) and several other organic compounds. Proposals have been made aiming at substitut- ing graphite for a single-phase SnO2-based ceramic with low resistiv...
| Autores: | , , , , , , , |
|---|---|
| Formato: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2012 |
| País: | Brasil |
| Recursos: | Universidade Estadual Paulista (UNESP) |
| Repositorio: | Repositório Institucional da UNESP |
| Idioma: | inglés |
| OAI Identifier: | oai:repositorio.unesp.br:11449/123478 |
| Acesso em linha: | http://www.scirp.org/journal/PaperInformation.aspx?PaperID=19190#.VUzvoI5VhHw http://hdl.handle.net/11449/123478 |
| Access Level: | acceso abierto |
| Palavra-chave: | Tin Oxide Anodic Electrode Inconsumable Anode Microwave Sintering Electrical Resistivity |
| Resumo: | The Hall-Héroult process is used for alumina reduction by the use of graphite anodes even though it involves a high emission of carbon dioxide (CO2) and several other organic compounds. Proposals have been made aiming at substitut- ing graphite for a single-phase SnO2-based ceramic with low resistivity and chemical resistance to cryolite, which is characterized as an inconsumable anode, reducing pollutant emissions. To this end, a wide range of studies were carried out on SnO2-based ceramics modified with ZnO as a densification aid doped with the promoters of electrical conduc- tivity such as Nb2O5, Al2O3 and Sb2O3 through a mixture of oxides and hybrid sintering in a microwave oven. The pressed pellets were sintered in a microwave oven up to 1050°C under a constant heating rate of 10°C/min. After sin- tering, the density was determined by the Archimedes method, the phases were then characterized by X-ray diffraction, the microstructure and chemical composition resulting from the sintered SnO2-based ceramics were also investigated by field emission scanning electron microscopy (FE-SEM) coupled with an energy-dispersive X-ray spectroscopy (EDS) and the electrical properties were determined by the measurements of the electric field × current density. A single-phase ceramic was obtained with a relative density of above 90% and electrical resistivity of 6.1 Ω·cm at room temperature. The ceramics obtained in this study could be a potential candidate as an inconsumable anode to replace the current fused coke used in the reduction of alumina. |
|---|