Profundidade de polimerização de uma resina bulk fill fluida após adição de xilitol
Objective: To evaluate the depth of cure at different thicknesses of the Tetric® NFlow Bulk Fill composite resin with the addition of xylitol at different concentrations. Materials and Methods: The Tetric™ N-Flow Bulk Fill resin was mixed with xylitol concentrations (0% [Control], 2.5%, and 5% g/g)...
| Autor: | |
|---|---|
| Tipo de recurso: | tesis de maestría |
| Estado: | Versión publicada |
| Fecha de publicación: | 2023 |
| País: | Brasil |
| Institución: | Universidade Federal do Rio Grande do Norte (UFRN) |
| Repositorio: | Repositório Institucional da UFRN |
| Idioma: | portugués |
| OAI Identifier: | oai:repositorio.ufrn.br:123456789/55294 |
| Acceso en línea: | https://repositorio.ufrn.br/handle/123456789/55294 |
| Access Level: | acceso abierto |
| Palabra clave: | Resina composta Bulk fill fluida Xilitol Polimerização CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
| Sumario: | Objective: To evaluate the depth of cure at different thicknesses of the Tetric® NFlow Bulk Fill composite resin with the addition of xylitol at different concentrations. Materials and Methods: The Tetric™ N-Flow Bulk Fill resin was mixed with xylitol concentrations (0% [Control], 2.5%, and 5% g/g) by manual spatulation for 1 minute in a portable darkroom. Cylindrical samples were prepared in polymethyl methacrylate molds with diameters of 5 mm and thicknesses of 1 mm, 2 mm, 3 mm, and 4 mm at the proposed xylitol concentrations, totaling 12 groups (n=3), photoactivated for 10 seconds, and stored at 37°C for 24 hours. The specimens were subjected to Vickers microhardness testing, and the depth of cure was obtained by calculating the base/top ratio. Non-parametric Kruskal-Wallis tests were used to compare different thicknesses at the same concentration and different concentrations at the same thickness (p<0,05) using BioEstat 5.3 software. Results: There was no statistically significant difference between different thicknesses at the same concentration, as well as between different concentrations at the same thickness (p=1,000). All specimens exhibited adequate depth of cure (hardness ratio ≥80%), except for the samples with 4 mm thickness containing 2.5% and 5% xylitol, which showed average hardness ratios of 79% and 74%, respectively. Conclusion: Under the conditions of this study, it can be concluded that the addition of xylitol to a fluid bulk fill resin can affect the depth of cure at 4 mm. |
|---|